ASTM金属硬度换算表

张曦

洛   氏 金 钢 石			表  面   洛  氏  金   钢  石			维氏	布氏	抗拉强度
HRC	HRA	HRD	HR15N	HR30N	HR45N	HV	HB 10MM球
C	A	D	15N	30N	45N	HV	HB	óｂ
150kgf	60kgf	100kgf	15kgf	30kgf	45kgf		3000kgf	Mpa
68	85.6	76.9	93.2	84.4	75.4	940	—	—
67	85	76.1	92.9	8.36	74.2	900	—	—
66	84.5	75.4	92.5	82.8	73.3	865	—	—
65	83.9	74.5	92.2	81.9	72	832	739	—
64	83.4	73.8	91.8	81.1	71	800	722	—
63	82.8	73	91.4	80.1	69.9	772	705	—
62	82.3	72.2	91.1	79.3	68.8	746	688	—
61	81.8	71.5	90.7	78.4	67.7	720	570	—
60	81.2	70.7	90.2	77.5	66.6	697	654	—
59	80.7	69.9	89.8	76.6	65.5	674	634	2420
58	80.1	69.2	89.3	75.7	64.3	653	615	2330
57	79.6	68.5	88.9	74.8	63.2	633	595	2240
56	79	67.7	88.3	73.9	62	613	577	2160
55	78.5	66.9	87.9	73	60.9	595	560	2070
54	78	66.1	87.4	72	59.8	577	543	2010
53	77.4	65.4	86.9	71.2	58.6	560	525	1950
52	76.8	64.6	86.4	70.2	57.4	544	512	1880
51	76.3	63.8	85.9	69.4	56.1	528	496	1820
50	75.9	63.1	85.5	68.5	55	513	481	1760
49	75.2	62.1	85	67.6	53.8	498	469	1700
48	74.7	61.4	84.5	66.7	52.5	484	455	1640
47	74.1	60.8	83.9	65.8	51.4	471	443	1580
46	73.6	60	83.5	64.8	50.3	458	432	1520
45	73.1	59.2	83	64	49	446	421	1480
44	72.5	58.5	82.5	63.1	47.8	434	409	1430
43	72	57.7	82	62.2	46.7	423	400	1390
42	71.5	56.9	81.5	61.3	45.5	412	390	1340
41	70.9	56.2	80.9	60.4	44.3	402	381	1300
40	70.4	55.4	80.4	59.5	43.1	392	371	1250
39	69.9	54.6	79.9	58.6	41.9	382	362	1220
38	69.4	53.8	79.4	57.7	40.8	372	353	1180
37	68.9	53.1	78.8	56.8	39.6	363	344	1140
36	68.4	52.3	78.3	55.9	38.4	354	336	1110
35	67.9	51.5	77.7	55	37.2	345	327	1080
34	67.4	50.8	77.2	54.2	36.1	336	319	1050
33	66.8	50	76.6	53.3	34.9	327	311	1030
32	66.3	49.2	76.1	52.1	33.7	318	301	1010
31	65.8	48.4	75.6	51.3	32.5	310	294	970
30	65.3	47.7	75	50.4	31.3	302	286	950
29	64.8	47	74.5	49.5	30.1	294	279	930
28	64.3	46.1	73.9	48.6	28.9	286	271	900
27	63.8	45.2	73.3	47.7	27.8	279	264	880
26	63.3	44.6	72.8	46.8	26.7	272	258	860
25	62.8	43.8	72.2	45.9	25.5	266	253	850
24	62.4	43.1	71.6	45	24.3	260	247	820
23	62	42.1	71	44	23.1	254	243	810
22	61.5	41.6	70.5	43.2	22	248	237	790
21	61	40.9	69.9	42.3	20.7	243	231	770
20	60.5	40	69.4	41.5	19.6	238	226	760
注：本表给出的数值应被作为粗略的换算关系，在某些特定的应用条件下可能是不准确的。表中粗体的布氏硬度值高于ASTM  E10标准中推荐的布氏硬度试验的测试范围。除HRE及抗拉强度以外所有的换算关系都取自ASTM E140；抗拉强度的换算关系取自ASTM  A370；HRE的换算关系并非取自ASTM标准。

洛 　　　 氏				表   面    洛   氏			维 氏	布 氏	抗拉强度	布 氏
HRB	HRA	HRF	HRE	HR15T	HR30T	HR45T	HV	HB		HB
1.588mm球	金   钢    石			1.588mm 球				10mm 球		10mm 球
100kgf	60kgf	60kgf	100kgf	15kgf	30kgf	45kgf		3000kgf	Mpa	500kgf
B	A	F	E	15T	30T	45T	HV	HB	óｂ	HB
100	61.5	—	—	93.1	83.1	72.9	240	240	800	201
99	60.9	—	—	92.8	82.5	71.9	234	234	785	195
98	60.2	—	—	92.5	81.8	70.9	228	228	750	189
97	59.5	—	—	92.1	81.1	69.9	222	222	715	184
96	58.9	—	—	91.8	80.4	68.9	216	216	705	179
95	58.3	—	—	91.5	79.8	67.9	210	210	690	175
94	57.6	—	—	91.2	79.1	66.9	205	205	675	171
93	57	109.2	—	90.8	78.4	65.9	200	200	650	167
92	56.4	108.7	—	90.5	77.8	64.8	195	195	635	163
91	55.8	108.2	—	90.2	77.1	63.8	190	190	620	160
90	55.2	107.5	—	89.9	76.4	62.8	185	185	615	157
89	54.6	107.2	—	89.5	75.8	61.8	180	180	605	154
88	54	106.7	—	89.2	75.1	60.8	176	176	590	151
87	53.4	106.3	—	88.9	74.4	59.8	172	172	580	148
86	52.8	106	—	88.6	73.8	58.8	169	169	570	145
85	52.3	105.5	—	88.2	73.1	57.8	165	165	565	142
84	51.7	105	—	87.9	72.4	56.8	162	162	560	140
83	51.1	104.5	—	87.6	71.8	55.8	159	159	550	137
82	50.6	104	—	87.3	71.1	54.8	156	156	530	135
81	50	103.5	—	86.9	70.4	53.8	153	153	505	133
80	49.5	103	—	86.6	69.7	52.8	150	150	495	130
79	48.9	102.5	—	86.3	69.1	51.8	147	147	485	128
78	48.4	102	—	86	68.4	50.8	144	144	475	126
77	47.9	101	—	85.6	67.7	49.8	141	141	470	124
76	47.3	100.5	—	85.3	67.1	48.8	139	139	460	122
75	46.8	100	—	85	66.4	47.8	137	137	455	120
74	46.3	99.2	—	84.7	65.7	46.8	135	135	450	118
73	45.8	98.5	—	84.3	65.1	45.8	132	132	440	116
72	45.3	98	—	84	64.4	44.8	130	130	435	114
71	44.8	97.5	100	83.7	63.7	43.8	127	127	425	112
70	44.3	97	99.5	83.4	63.1	42.8	125	125	420	110
69	43.8	96.5	99	83	62.4	41.8	123	123	415	109
68	43.3	96	98	82.7	61.7	40.8	121	121	405	108
67	42.8	95.5	97.5	82.4	61	39.8	119	119	400	106
66	42.3	95	97	82.1	60.4	38.7	117	117	395	104
65	41.8	94.5	96	81.8	59.7	37.7	116	116	385	102
64	41.4	94	95.5	81.4	59	36.7	114	114	—	100
63	40.9	93	95	81.1	58.4	35.7	112	112	—	99
62	40.4	92.6	94.5	80.8	57.7	34.7	110	110	—	98
61	40	92	93.5	80.5	57	33.7	108	108	—	96
60	39.5	91.5	93	80.1	56.4	32.7	107	107	—	95
59	39	91	92.5	79.8	55.7	31.7	106	106	—	94
58	38.6	90.5	92	79.5	55	30.7	104	104	—	92
57	38.1	89.8	91	79.2	54.4	29.7	103	103	—	91
56	37.7	89	90.5	78.8	53.7	28.7	101	101	—	90
55	37.2	88.5	90	78.5	53	27.7	100	100	—	89
54	36.8	88	89.5	78.2	52.4	26.7	—	—	—	87
53	36.3	87.2	89	77.9	51.7	25.7	—	—	—	86
52	35.9	86.7	88	77.5	51	24.7	—	—	—	85
51	35.5	86.3	87.5	77.2	50.3	23.7	—	—	—	84
50	35	85.7	87	76.9	49.7	22.7	—	—	—	83
49	34.6	85.2	86.5	76.6	49	21.7	—	—	—	82
48	34.1	84.6	85.5	76.2	48.3	20.7	—	—	—	81
47	33.7	84.1	85	75.9	47.7	19.7	—	—	—	80
46	33.3	83.5	84.5	75.6	47	18.7	—	—	—	80
45	32.9	82.9	84	75.3	46.3	17.7	—	—	—	79
44	32.4	82.3	83.5	74.9	45.7	16.7	—	—	—	78
43	32	81.7	82.5	74.6	45	15.7	—	—	—	77
42	31.6	81.2	82	74.3	44.3	14.7	—	—	—	76
41	31.2	80.6	81.5	74	43.7	13.6	—	—	—	75
40	30.7	80	81	73.6	43	12.6	—	—	—	75
39	30.3	79.5	80	73.3	42.3	11.6	—	—	—	74
38	29.9	79	79.5	73	41.6	10.6	—	—	—	73
37	29.5	78.4	79	72.7	41	9.6	—	—	—	72
36	29.1	77.9	78.5	72.3	40.3	8.6	—	—	—	72
35	28.7	77.4	78	72	39.6	7.6	—	—	—	71
34	28.2	76.9	77	71.7	39	6.6	—	—	—	70
33	27.8	76.4	76.5	71.4	38.3	5.6	—	—	—	69
32	27.4	75.8	76	71	37.6	4.6	—	—	—	69
31	27	75.3	75.5	70.7	37	3.6	—	—	—	68
30	26.6	74.8	75	70.4	36.3	2.6	—	—	—	67

PHR系列洛氏硬度计
原理·符合洛氏硬度试验定义
精确·精度与台式机相同
轻便·重量只有台式机的1％
灵活·可在室内外各种场合使用
标尺·可测试洛氏硬度15个标尺
可测试表面洛氏硬度15个标尺
洛氏硬度标尺的选择（按材料种类）
标尺符号	压  头	总试验力	表盘数字	标尺的典型应用
		(kgf)
A	金钢石	60	C	高硬度或薄硬材料。如硬质合金、薄硬
				钢片、渗碳后的淬硬钢。
B	1.588mm球	100	B	中低硬度材料。如退火的中低碳钢、不锈
				钢、铜合金、超硬铝合金、可锻铸铁等。
C	金钢石	150	C	淬火及低温回火钢材、冷硬铸铁、珠光体可
				可锻铸铁、钛合金、硬度值超过HRB100的材料
D	金钢石	100	C	中等渗层表面硬化钢、薄硬钢片、珠光体可锻
				可锻铸铁。
E	3.175mm球	100	B	铸铁、铝合金、镁合金、轴承合金。
F	1.588mm球	60	B	退火黄铜、紫铜、铝合金、软钢薄坂。
G	1.588mm球	150	B	铍青铜、磷青铜、可锻铸铁等HRB值接近
				100的材料。
H	3.175mm球	60	B	铝、锌、铅、锡等软金属。
K	3.175mm球	150	B	软金属薄片、轴承合金。
L	6.350mm球	60	B
M	6.350mm球	100	B
P	6.350mm球	150	B	轴承合金及其他极软或极薄的材料。采用不
R	12.70mm球	60	B	产生测砧效应的最大试验力及最小球压头。
S	12.70mm球	100	B
V	12.70mm球	150	B
15N	金钢石	15	N-T	浅层表面硬化钢；小零件；刀口、锯口；
30N	金钢石	30	N-T	厚度薄至0.15mm的硬钢带及要求压痕
45N	金钢石	45	N-T	尽量小的高硬度工件。
15T	1.588mm球	15	N-T	软钢、不锈钢、铜及铜合金、铝合金薄
30T	1.588mm球	30	N-T	板带、薄壁管材、小零件、冲压件及要
45T	1.588mm球	45	N-T	求压痕尽量小的中低硬度工件。
资料来源：ASTME  18-07《金属洛氏硬度和表面洛氏硬度标准试验方法》